Product Details:
Payment & Shipping Terms:
|
| Material Grade: | Mo-Re 1,Mo-Re 2, Supertherm,TMA4700, ASTM A1002,Mo-Re 10, | Production Process: | Spun Cast |
|---|---|---|---|
| Working Temperature: | Up To 2400F | Surface Finish: | Fully Machining To Ra1.6, Ra3.2 |
| Certification: | ISO 9001 | Roller Diameter: | 50-900mm |
| High Light: | centrifugal casting products,centrifugally cast iron pipe |
||
Mo Re 1 Alloy Cast Furnace Rollers
The Furnace Rollers are made from Mo Re 1,which can resist 2400F high temperture.
Special Features:
1.The chemlcal elements are checked by our Spetrometer；
2.The roller diameter: 50mm - 500mm; Length: less than 400mm.
3.The furnace rollers can be fully machined.
4.Centrifugal Cast process is kind of highly efficiengt production process ,which can achieve sound castings and make the production time as short as possible;
5The furnace rollers can be made as per customer drawings.
6.Material grades:
| ASTM | Alloy | C | Cr | Ni | Other | Description |
| 30/50 W | 22H® | 0.45 | 30 | 50 | W 4 | The alloy is wholly austenitic and is intended for use at elevated temperatures up to 2200° F (1204° C). |
| HP+W | MO-RE®1 | 0.45 | 25 | 35 | W 1.5 | Tungsten addition increases creep strength. Useful to 2000°/2100° F (1093°/1149°C). MO-RE® 1 is a good option for use in severe high temperature furnace roll and radiant tube applications. |
| 28/48 W+Co | Super 22H® | 0.45 | 28 | 48 | W 5 Co 3 | Alloy of choice for extreme high temperature service to 2200° F (1066° to 1200° C). |
| MO-RE®2 | 0.2 | 33 | 50 | W 17+Al | Exceptional strength and oxidation resistance to 2400° F (1315° C). | |
| HP Nb LC | MO-RE®9 | 0.09 | 25 | 35 | Nb 1 | MO-RE ® 9 is used primarily for parts located outside of furnace such as transfer lines and headers. It is designed for applications which require high ductility after aging. |
| A608 | MO-RE ®10 | 0.4 | 25 | 35 | Nb 1.2 | MO-RE ®10 is a fully austenitic alloy with controlled additions of columbium (niobium) for ethylene pyrolysis tubing. It has improved high temperature strength and resistance to carburization and oxidation up to 2000° F (1093° C). |
| HP+Nb+MA | MO-RE ®10 MA | 0.45 | 25 | 35 | Nb 1.2 Ti Rare Earths | MO-RE ®10 MA is microalloyed with additions of columbium (niobium), zirconium and titanium for improved high temperature strength and resistance to carburization and oxidation up to 1975 °F (1079 °C). Microalloying produces fine, stable carbides which retard dislocation movement, thereby increasing elevated temperature strength and creep resistance. Intended for ethylene pyrolysis applications. |
| A297 A351 | MO-RE ®21 | 0.1 | 20 | 32 | Nb 1.2 | Low carbon, columbium strengthened alloy with excellent thermal fatigue / thermal shock resistance. MO-RE 21 is a cast alternative to wrought alloy 800HT. |
| MO-RE ®35 MA | 0.45 | 28 | 36 | Al, Rare Earths | MO-RE ® 35 MA is a fully austenitic heat resistant alloy developed by Duraloy primarily for plate heat treating furnace roll applications. MO-RE ®35 MA is microalloyed with additions of aluminum, titanium and proprietary rare earth additions for improved creep strength at furnace operating temperatures. Microalloying produces fine, stable carbides which retard dislocation movement, thereby increasing elevated temperature strength and creep resistance. Primarily intended for use in plate furnace rolls. | |
| 35/45 Nb+MA | MO-RE® 40 MA |
0.45 | 34 | 45 | Nb 1 Ti Rare Earths | MO-RE ®40MA has exceptional resistance to carburization and oxidation up to 2100 °F (1149 °C). |
| MO-RE ®49 | 0.4 | 23 | 5 | MO-RE ®49 is an iron-chromium-nickel heat resistant alloy developed for aerospace tooling. | ||
| MO-RE® 2150 | These Cr-Ni-W alloys are produced to unique chemistries for each customer to work in their dry tunnel furnace roll application. | |||||
| A1002 | Nickel Aluminide | R&D 100 Award Winner Nickel-Aluminum alloy, developed and patented by Oak Ridge National Laboratory and licensed to Duraloy. Alloy shows exceptional resistance to creep at elevated temperatures. Also shows strong resistance to carburization in service. Excellent selection for plate hardening furnace rolls. | ||||
| SUPERTHERM® | 0.45 | 25 | 35 | Co 15 W 5 | Supertherm exhibits excellent oxidation resistance & high temperature strength to 2300° F (1260 °C). Supertherm is an excellent alloy for use in high temperature press platens or other applications where high temperature strength is critical. | |
| TMA®4505 | 0.3 | 20 | 25 | W, Nb additons | TMA4505 is a heat resistant alloy developed by Duraloy for SuperPlastic and Hot Press tooling applications. It is a modification of ASTM A297 Grade HN with improved properties. | |
| HK-40+MA | TMA®4700 | 0.4 | 25 | 20 | W, Nb & Ti additions | TMA®4700 is an iron-chromium-nickel (modified HK type) heat resistant alloy. TMA ®4700 is microalloyed with additions of columbium (niobium), tungsten, titanium and rare earths for superior stress rupture properties to 2000°F (1093°C). Microalloying produces fine, stable carbides which retard dislocation movement, thereby increasing elevated temperature strength and creep resistance. |
| TMA®4701 | R&D 100 Award Winner heat resistant alloy developed by Duraloy. TMA®-nickel (modified HK type). TMA® 4701 has a proprietary, microalloyed, computer designed chemistry which gives the alloy better high temperature creep properties than similar alloys. It is intended primarily for reforming applications. | |||||
| HP+Nb+MA (LoSil) | TMA®6300 | 0.4 | 25 | 35 | Nb 1.2 Ti Rare Earths | TMA® 6300 is a fully austenitic heat resistant alloy. TMA®6300 is microalloyed with additions of columbium (niobium), titanium and rare earths for improved high temperature strength and resistance to carburization and oxidation up to 1950 ° F (1066 ° C). Microalloying produces fine, stable carbides which retard dislocation movement, thereby increasing elevated temperature strength and creep resistance. Intended primarily for reforming applications. |
| HP+Nb+MA (LoSil) | TMA® 6301 | 25 | 35 | Nb 1.2 Ti Rare Earths | R&D 100 Award Winner heat resistant alloy developed by Duraloy. TMA ®6301has a proprietary, microalloyed, computer designed chemistry which gives the alloy better high temperature creep properties than similar alloys. It is intended primarily for reforming applications. |
Step 1: Getting orders.
Step 2: Process design by technical department
Step 3: Purchase of raw materials and pattern making &checking
Step 4: Inspection of raw materials
Step 5: Melting by middle-frequency induction furnaces
Step 6: Ladle analysis by Spectrometer
Step 7: De-oxidization, slag-removal, tapping
Step 8: Pouring
Step 9: Openning & fettling
Step 10: Surface & dimensional check
Step 11: Heat treatment
Step 12: Inspection of physical property (UT test,MT test, hardness,impact value, matrix structure)
Step 13: Packing
Step 14: Shipping
1. 16-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.
Contact Us for further information about products & service:
Mr.John Liu
Project Manager
Tel: 0086-188 0059 6372
Fax: 0086-510-6879 2172
Email :cast@ebcastings.com; ebcastings@163.com
Skype ID:julia.zhu26
QQ: 217 039 6403
What's app: 0086-130 930 23772
Eternal Bliss Alloy Casting & Forging Co.,LTD.
Add.: J-Sci-Tech Park, Binhu District,Wuxi,214122, Jiangsu,China
Our Inspection Video:
Contact Person: Juliet Zhu
Tel: 0086-13093023772