Product Details:
Payment & Shipping Terms:
|
| Material: | Heat-resistant Cast Iron | Standard: | QT500-7 |
|---|---|---|---|
| Dimensions: | Drawing | Machine Type: | Crusher |
| Hardness: | 170-230HB | Surface Treatment: | Maching |
| Capactities: | 10 Tons,20 Tons,25 Tons,etc | Process: | Sand Cast Process |
| High Light: | QT500-7 Heat Resistant Cast Steel,QT500-7 slag pot,QT500-7 Heat resistant Cast Iron |
||
QT500-7 Slag Pots Ductile Iron Slag Pot Sand Casting Slag Tank
Product Description:
The Slag Pot is an important equipment in steelmaking production. It is a container for high-temperature slag produced during the smelting process of steel. It has a bowl-shaped container with lifting trunnions on both sides.
Slag Pot purchased by metallurgical companies generally use the traditional casting process, which has a long manufacturing cycle, short service life, and a large number of scraps. Great Wall Cast Steel has increased innovation in the production of slag tanks, and its slag tanks have a short casting period and a long service life Strong anti-deformation ability.
The Trends for Material Selection:
Due to obvious advantages in terms of service life,maintenance and cost-efficiency, cast steel has been becoming more significant in the melting pot construction over the last few years against both materials, spheroidal cast-iron and lamellar graphite cast-iron. In comparison with other materials, cast steel offers excellent repair possibilities as it is well-suited to welding.
Detailed Description:
Material: Heat Resistant Cast Iron, QT500-7, etc;
Quality Level: As per National Standard & International Standards.
Production Process: Sand Process Heat-treatment Process.Including machining process,such as drilling and tapping holes.
Special Features:
1. We can make big size alloy steel castings with Sodium Silicate Sand Process.
2. We can supply finished alloy steel castings with heat-treatment and machining process.
3. We can produce alloy Steel castings as per ASTM A27, GB/T 20878, DIN 17440, DIN 17224, AISI, ASTM,JIS SUH35, NF A35-572/584, BS970,BS1449, ISO 683/13.
4. The biggest steel castings we can achieve so far is 300 tons per piece.
|
GB
|
Tensile Strength
σb/Mpa (≥)
|
Yield Point
σs/Mpa (≥)
|
Elongation
δ5/%(≥)
|
Hardness(HBS)
|
|
QT400-18
|
400
|
250
|
18
|
130~180
|
|
QT500-7
|
500
|
320
|
7
|
170~230
|
|
QT600-3
|
600
|
380
|
3
|
190~270
|
|
QT700-2
|
700
|
440
|
2
|
225~305
|
|
Chemical Composition(%)
|
C
|
Si
|
Mn
|
P
|
S
|
Mg
|
Re
|
|
QT400-18
|
3.6~3.8
|
2.3~2.7
|
≤0.5
|
≤0.03
|
≤0.05
|
0.03~0.05
|
0.02~0.03
|
|
QT500-7
|
3.4~3.9
|
2.0~2.9
|
≤0.6
|
≤0.03
|
≤0.05
|
0.03~0.10
|
0.03~0.10
|
|
QT600-3
|
3.4~3.8
|
2.0~2.8
|
0.3~0.7
|
≤0.03
|
≤0.05
|
0.035~0.05
|
0.025~0.045
|
|
QT700-2
|
3.5~4.0
|
2.0~2.6
|
0.5~0.9
|
≤0.03
|
≤0.05
|
0.035~0.065
|
0.035~0.065
|