| Material: | Alumina Ceramic | Type: | Ceramic Plates |
|---|---|---|---|
| Dimensions: | According To Customer Drawings | Color: | White |
| Bulk Density: | 3.6-3.63g/cm3 | Moh's Hardness: | 9 |
| Water Absorption: | 0.01% | Shape: | Curved |
| Usag: | Conveying Cchute Liner | Mode Of Shaped: | Dry Pressing |
| Forming Temperature: | 1530℃ | Application: | Refractory, Industrial Ceramic |
| High Light: | Rubber ceramic wear liner,Abrasion Resistant ceramic wear liner,Curved Mining Chute Lining |
||
Mining Chute Lining Abrasion Resistant Rubber Ceramic Wear Liner
Application:
1.Silicon nitride and silicon carbide beams have excellent high-temperature flexural strength, creep resistance and oxidation resistance; mainly used in sanitary ceramics, high-voltage electrical porcelain, filters, quartz crucibles; shed plates and fish-shaped plates which are widely used in daily-use ceramic Industry; protection tube is used for temperature measurement in various industries; special-shaped products and burner sleeves are widely used in various kiln and mechanical engineering.
|
Item
|
Unit
|
Data
|
|
Bulk density
|
g/cm3
|
2.75-2.82
|
|
Porosity
|
%
|
10-12
|
|
Compressive strength
|
MPa
|
600-700
|
|
Flexural strength
|
MPa
|
160-180
|
|
Young's modulus
|
Gpa
|
220-260
|
|
Thermal Conductivity
|
W/MK
|
15
|
|
Thermal expansion coefficient: 20-1000 ℃
|
10-6K-1
|
5.0
|
|
Maximum use temperature
|
C
|
1500
|
|
SiC
|
%
|
60-80
|
|
Silicon nitride
|
%
|
20-40
|
|
Material Data:
|
||
|
Item
|
Unit
|
Data
|
|
Bulk density
|
g/cm3
|
2.60-2.74
|
|
Porosity
|
%
|
15
|
|
Compression strength
|
MPa
|
≥600
|
|
Flexural strength
|
MPa
|
90-100
|
|
Young modulus |
Gpa
|
240
|
|
Thermal conductivity
|
W/MK
|
24
|
|
Coefficient of thermal expansion 20-1000C
|
10-6K-1
|
4.8
|
|
Max using temperature
|
C
|
1650
|
|
SiC
|
%
|
98.5
|
|
3.Sintering process of silicon carbide ceramics mainly includes: pressureless sintering, reaction sintering, hot-pressing sintering and hot isostatic pressing. Among them, reaction sintering and pressureless sintering are more commonly used. The properties of silicon carbide ceramics also vary depending on the sintering method.
Pressureless sintering can produce parts with complex shapes and large-sized silicon carbide ceramic parts. |
||
|
Material Data:
|
||
|
Item
|
Unit
|
SSIC
|
|
Density
|
g/cm3
|
3.10-3.15
|
|
Hardness
|
HRA
|
92--94
|
|
Apparent porosity
|
%
|
<0.2
|
|
Compressive strength
|
Mpa
|
≥2200
|
|
Flexural strength
|
Mpa
|
≥400
|
|
Elastic Modulus
|
Gpa
|
400
|
|
Thermal conductivity (20 C)
|
W/m k
|
120--150
|
|
Thermal expansion coefficient
|
10 -6 1/c
|
4
|
|
Maximum use temperature
|
c
|
1600
|
|
4.Reaction sintering is currently the most commonly used sintering method for functional ceramics and special ceramics. Because of its relatively simple production process and low production cost, application:silicon carbide seals, silicon carbide bearings,silicon carbide nozzles ect.
|
||
|
Material Data:
|
||
|
Item
|
Unit
|
RBSIC
|
|
Bulk density
|
g/cm3
|
≥3.03
|
|
hardness
|
HRA
|
91--93
|
|
Apparent porosity
|
%
|
<0.2
|
|
Flexural strength
|
Mpa
|
≥350
|
|
Compressive strength
|
Mpa
|
≥2000
|
|
Thermal Conductivity
|
W/m k
|
50~110
|
|
Thermal expansion coefficient
|
10 -6 1/C
|
4
|
|
Elastic Modulus
|
GPa
|
350
|
|
Free silicon content
|
%
|
<12
|
|
Maximum use temperature
|
C
|
1000
|
|
Features of Rubber Ceramic Wear Liners, Composite Lining Plate
|
|
|
1
|
Extend the service life of your facilities
|
|
2
|
Excellent wear and abrasion resistance
|
|
3
|
Reduce noise
|
|
4
|
Cost effective
|
|
5
|
Customized size to suit
|
|
6
|
Reduce maintainance cost and down time
|
Product Details Picture:
Contact Person: Juliet Zhu
Tel: 0086-13093023772