In January 2017, we produced Medium manganese MQT Mn7 arc plate castings for crushers. 1.There are two kinds of the arc plate castings.The thickness is 22mm and 30mm.And the weights are about 55kg and 75kg. 2.The material of the castings is MQT Mn7.Chemical composition is shown as below: 3.We ... Read More
|
| |
In September 2016, we produced ZG60Cr5Mo wear plates. 1.We adopted the sand cast process to make the plates.The size is 690 x 600 x 20mm.The weight of each plate is about 60kg. 2.The material of the liners is ZG60Cr5Mo.The hardness required is more than HRC48.The actual hardness is about HRC53. 3.We ... Read More
|
| |
In January 2017, we produced 1.4865 radiant tubes for South Asian customer.The radiant tube is for carburizing treatment of precision gears. 1.There are two sizes for the radiant tubes:Birlec Radiant Tubeφ115 x 9 x 1600 ， Gibbons Rad Tubeφ170 x 9 x 1500. Chemical composition is shown as below: 2.We ... Read More
|
| |
In February 2017, we produced dispenser cone castings &316L adapter forgings, shipped to Australia. 1.Chemical composition is shown as below: 2.The weight of the dispenser and adapter are about 45kg and 5kg.We adopted investment cast process to make the castings. 3.We did ultrosonic spray coating on ... Read More
|
| |
June 2017, we produced aluminum castings for bearings and rubber sets. 1.The size of bearing Al castings:OD220 x ID120 x 78mm, The size of rubber set Al castings:OD220 x ID53 x 70mm. 2.We adopted sand process to make the castings.The material of the aluminum castings is 6061-T6.Chemical composition ... Read More
|
| |
In August 2016, we produced 50-ton melting kettle castings for Malaysian customer for the third time. 1.The size of the melting kettle casting:φ3632 xφ3224 x 1562mm.The material is ZG230-450( BS3100 A4).Chemical composition is shown as below: Mechanical properties are shown as below: Tensile ... Read More
|
| |
In March 2017, we produced Jacket Cover cobalt-based alloy castings, delivered to Australia. 1.The material grade for castings: AMS5387C UNS R30006,high temperature alloy.We adopted investment cast process to make the castings. 2.The Jacket Cover casting is about 800mm long and is U-shape, 8mm thick... Read More
|
| |
In July 2017, we produced high-temperature cobalt-based alloy rods for European customer. 1.The material for Cobalt-based alloy rods is Co193(Tribaloy T-400 Alloy), which chemical composition is shown in the following Figure: 2.We adopted investment cast process to make the bars.Hardness:HRC52. 3... Read More
|
| |
In December 2016, we produced 400 ZL101 Aluminum castings according to customer’s requirement. 1.The material is ZL101, equivalent to LM25.The weight of this casting is about 2kg. 2.Aluminum alloy melting point is low and casting performance is good.The castings accuracy and internal quality ... Read More
|
| |
On March 2017, we produced two UmCo50 cobalt-based alloy chute castings, delivered to South Asia. 1.The casting size is 660 x 490 x 300, quantity: 2 pieces, the total weight of about 400kg. The material of the castings: UmCo50, for the high temperature alloy.We adopted sand cast process to make the ... Read More
|