cobalt alloy 1 Coating Cobalt Alloy Castings Customized Investment Forging Parts

cobalt alloy 1 Coating Customized Investment Forging Parts Heat-Resistance Steel 316L EB3385

We produce High Temperature Superalloy Castings Parts with centrifugal cast process, investment process and resin sand cast process.

United States Patent 3,418,111 COBALT BASE ALLOY Robert B. Herchenroeder, Kokomo, Ind., assignor to Union Carbide Corporation, a corporation of New ork No Drawing. Filed Oct. 27, 1966, Ser. No. 589,822 3 Claims. (Cl. 75171) This invention relates to cobalt base alloys. More particularly, this invention relates to cobalt-chromiumtungsten-nickel alloys containing relatively small amounts of lanthanum which are characterized by improved oxidation resistance at high temperatures in addition to having excellent high temperature mechanical properties.

Table 1 : Standard Cobalt cobalt alloy Alloy 

Hastelloy C22®(UNS N06022)(Max.)

C

MN

P

S

Si

Cr

Ni

Mo

CO

Fe

W

V

0.015

0.5

0.02

0.02

0.08

20.0-22.5

Bal.

12.5-14.5

2.5

2.0-6.0

2.5-3.5

0.35

Hastelloy C276®(UNS N10276)(Max.)

C

MN

P

S

Si

Cr

Ni

Mo

CO

Fe

W

V

0.01

1

0.04

0.03

0.08

14.5-16.5

Bal.

15.0-17.0

2.5

4.0-7.0

3.0-4.5

0.35

Hastelloyx®(UNS N06002)(Max.)

C

MN

P

S

Si

Cr

Ni

Mo

CO

Fe

W

other

0.05-0.15

1

0.04

0.03

1

20.5-23.0

Bal.

8.0-10.0

0.5-2.5

17.0-20.0

0.2-1.0

/

Monel 400®(UNS NO4400) (Max.)

C

MN

S

Si

Ni

Cu

Fe

0.3

2

0.024

0.5

63 min

28-34

2.5

Monel M400®(UNS NO4400)(Max.)

C

MN

S

Si

Ni

Cu

Fe

0.3

2

0.024

0.5

63-70

28-34

2.5

Monel R405®(UNS NO4405)(Max.)

C

MN

S

Si

Ni

Cu

Fe

0.3

2

0.025-0.06

0.5

63.0min

28-34

2.5

Monel K500®(UNS NO5500)(Max.)

C

MN

S

Si

Ni

Cu

Ti

AI

Fe

0.1

2

0.01

0.5

63min

27-33

0.86

2.3-3.15

2

Inconel 600(UNS NO6600)(Max.)

C

MN

S

Si

Cr

Ni

Cu

Fe

0.15

1

0.015

0.5

14-17

72 min

0.5

6.0-10.0

Inconel 601(UNS NO6601)(Max.)

C

MN

Si

Cr

Ni

CO

AI

Fe

0.05

0.3

0.2

22.5

61.5min

5

1.4

14.1

Inconel 718(UNS NO7718)(Max.)

Cr

Ni

Mo

CO

Cb+Ta

Ti

AI

Fe

19

52.5min

3.05

5

5.13

0.9

0.5

18.5

Chemical Analysis of Incoloy 800® uns(N08800)

C

Cr

Ni

Ti

AI

Fe

Grain

0.1 max

19.0-23.0

30.0-35.0

0.15-0.6

0.15-0.6

39.5min

/

Incoloy800H® UNS(N08810)

C

Cr

Ni

Ti

AI

Fe

Grain

0.05-0.1

19.0-23.0

30.0-35.0

0.15-0.60

0.15-0.60

39.5min

5or coarser

Incoloy800HT® UNS(N08811)

C

Cr

Ni

Ti

AI

Fe

Grain

0.06-0.10

19.0-23.0

30.0-35.0

0.25-0.60

0.25-0.60

39.5min

5or coarser

Dimensions:as per drawings

 

Production Process

 

Step 1: Getting orders.

 

Step 2: Process design by technical department

 

Step 3: Purchase of raw materials and pattern making &checking

 

Step 4: Inspection of raw materials

 

Step 5: Melting by middle-frequency induction furnaces

 

Step 6: Ladle analysis by Spectrometer

 

Step 7: De-oxidization, slag-removal, tapping

 

Step 8: Pouring

 

Step 9: Openning & fettling

 

Step 10: Surface & dimensional check

 

Step 11: Heat treatment

 

Step 12: Inspection of physical property (UT test,MT test, hardness,impact value µstructure)

 

Step 13: Packing

 

Step 14: Shipping

 

1. 16-year Foundry Operation Experience.

2. Friendly & High Efficient Technical & Commercial Communication.

3. Professional Export Practices: Have Exported to +60 Overseas Countries.

 

 

Our Trade Show

 

Our booth No. 14-A29-5 in Newcast 2015,Germany

Hall 14, Stand No.A29-5.

 

 

Contact Us for further information about products & service:

Mr.John Liu

Project Manager

Cell: 0086-130 930 23772(What's App)

Tel: 0086-188 0059 6372

Fax: 0086-510-6879 2172

E-mail: cast@ebcasting.com； ebcastings@163.com

Skype ID:julia.zhu26

QQ: 217 039 6403

www.ebcastings.com


Eternal Bliss Alloy Casting & Forging Co.,LTD.

Add.: J-Sci-Tech Park, Binhu District,Wuxi,214122, Jiangsu,China