The as-cast samples of FSX-414 Co-based superalloy were heat treated at the standard solution and aging heat treatment cycles. Specimens for joining were cut from the as-cast ingot. Transient liquid phase (TLP) bonding was carried out at the standard solution cycle, using MBF-30 interlayer. Also, bonded specimens were homogenized at the standard aging condition
We produce High Temperature Superalloy Castings Parts with centrifugal cast process, precision cast process and resin sand cast process.
Table 1 : Standard Cobalt cobalt alloy Alloy
Co | Cr | C | W | Mo | Ni | Si | B | Fe | Mn | Others | |
cobalt alloy 1 | BAL | 33 | 2.45 | 13 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 3 | BAL | 31 | 2.5 | 13 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 4 | BAL | 31.5 | 1 | 14 | - | 2.0* | 1 | - | 2.0* | 1 | - |
BAL | 28 | 1.2 | 5 | - | 3.0* | 1 | - | 2.5* | 1 | - | |
cobalt alloy 12 | BAL | 29 | 1.85 | 9 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 20 | BAL | 33 | 2.45 | 17.5 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 21 | BAL | 27 | 0.25 | - | 5.5 | 2.5* | 1 | - | 3.0* | 1 | - |
cobalt alloy 31 | BAL | 26 | 0.5 | 7.5 | - | 10.5 | 1 | - | 2.0* | 1 | - |
cobalt alloy 190 | BAL | 26 | 3.3 | 14 | - | 1.0 | 1 | - | 8.0 | 0.5 | - |
cobalt alloy 238 | BAL | 26 | 0.1 | - | 3 | - | 1 | - | 20.0 | 1 | - |
cobalt alloy 306 | BAL | 25 | 0.4 | 2 | - | 6.0 | 1 | - | 4.0* | 1 | Nb=5 |
94 | BAL | 28 | 1 | 19 | - | 5.0 | 1 | - | 2.5* | 1 | V=1 |
cobalt alloy F | BAL | 25.5 | 1.75 | 12.25 | - | 22.5 | 1 | - | 1.5* | - | - |
cobalt alloy SF1 | BAL | 19 | 1.3 | 13 | - | 13 | 3 | 2.5 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF6 | BAL | 19 | 0.7 | 7 | - | 13 | 2.5 | 1.7 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF12 | BAL | 19 | 1 | 9 | - | 13 | 3 | 2 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF20 | BAL | 19 | 1.5 | 15 | - | 13 | 3 | 3 | 2* | 0.5 | Cu=0.5 |
TRIBALOY T400 | BAL | 8 | 0.1* | - | 28 | 3* | 2.4 | - | 3* | - | - |
TRIBALOY T800 | BAL | 17 | 0.1* | - | 28 | 3* | 3.2 | - | 3* | - | - |
DELORO 15 | - | - | 0.06* | - | - | BAL | 2.0 | 1.05 | 1.5* | 20 | Cu=20 |
DELORO 22 | - | 0.70 | 0.10 | - | - | BAL | 2.3 | 1.75 | - | - | - |
DELORO 40 | - | 7.0 | 0.10 | - | - | BAL | 3.5 | 2.25 | - | - | - |
DELORO 50 | - | 10.25 | 0.45 | - | - | BAL | 4.0 | 1.85 | 4.0 | - | - |
DELORO 60 | - | 14.25 | 0.6 | - | - | BAL | 2.0 | 3.5 | 4.0 | - | - |
DELORO 625 | - | 22 | 0.1 | - | 9 | BAL | - | - | 5 | - | - |
NISTELLE C | - | 16.5 | 0.12* | 4.5 | 17 | BAL | 0.7 | - | 6.0 | - | - |
TRIBALOY T700 | - | 15 | 0.10* | - | 32 | BAL | 3.25 | - |
Hastelloy C22®(UNS N06022)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V | |
0.015 | 0.5 | 0.02 | 0.02 | 0.08 | 20.0-22.5 | Bal. | 12.5-14.5 | 2.5 | 2.0-6.0 | 2.5-3.5 | 0.35 | |
Hastelloy C276®(UNS N10276)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V | |
0.01 | 1 | 0.04 | 0.03 | 0.08 | 14.5-16.5 | Bal. | 15.0-17.0 | 2.5 | 4.0-7.0 | 3.0-4.5 | 0.35 | |
Hastelloyx®(UNS N06002)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | other | |
0.05-0.15 | 1 | 0.04 | 0.03 | 1 | 20.5-23.0 | Bal. | 8.0-10.0 | 0.5-2.5 | 17.0-20.0 | 0.2-1.0 | / | |
Monel 400®(UNS NO4400) (Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.024 | 0.5 | 63 min | 28-34 | 2.5 | ||||||
Monel M400®(UNS NO4400)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.024 | 0.5 | 63-70 | 28-34 | 2.5 | ||||||
Monel R405®(UNS NO4405)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.025-0.06 | 0.5 | 63.0min | 28-34 | 2.5 | ||||||
Monel K500®(UNS NO5500)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Ti | AI | Fe | ||||
0.1 | 2 | 0.01 | 0.5 | 63min | 27-33 | 0.86 | 2.3-3.15 | 2 | ||||
Inconel 600(UNS NO6600)(Max.) | ||||||||||||
C | MN | S | Si | Cr | Ni | Cu | Fe | |||||
0.15 | 1 | 0.015 | 0.5 | 14-17 | 72 min | 0.5 | 6.0-10.0 | |||||
Inconel 601(UNS NO6601)(Max.) | ||||||||||||
C | MN | Si | Cr | Ni | CO | AI | Fe | |||||
0.05 | 0.3 | 0.2 | 22.5 | 61.5min | 5 | 1.4 | 14.1 | |||||
Inconel 718(UNS NO7718)(Max.) | ||||||||||||
Cr | Ni | Mo | CO | Cb+Ta | Ti | AI | Fe | |||||
19 | 52.5min | 3.05 | 5 | 5.13 | 0.9 | 0.5 | 18.5 | |||||
Chemical Analysis of Incoloy 800® uns(N08800) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.1 max | 19.0-23.0 | 30.0-35.0 | 0.15-0.6 | 0.15-0.6 | 39.5min | / | ||||||
Incoloy800H® UNS(N08810) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.05-0.1 | 19.0-23.0 | 30.0-35.0 | 0.15-0.60 | 0.15-0.60 | 39.5min | 5or coarser | ||||||
Incoloy800HT® UNS(N08811) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.06-0.10 | 19.0-23.0 | 30.0-35.0 | 0.25-0.60 | 0.25-0.60 | 39.5min | 5or coarser | ||||||
Dimensions:as per drawings
Special Features: 1.Good surface finish; 2.We use Precision Cast Process to produce the Cobalt Based Superalloy parts. 3.We do high temperature solution treatment to achieve better wear performance. |
Step 1: Getting orders.
Step 2: Process design by technical department
Step 3: Purchase of raw materials and pattern making &checking
Step 4: Inspection of raw materials
Step 5: Melting by middle-frequency induction furnaces
Step 6: Ladle analysis by Spectrometer
Step 7: De-oxidization, slag-removal, tapping
Step 8: Pouring
Step 9: Openning & fettling
Step 10: Surface & dimensional check
Step 11: Heat treatment
Step 12: Inspection of physical property (UT test,MT test, hardness,impact value µstructure)
Step 13: Packing
Step 14: Shipping
1. 16-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.
MOQ: | 30 kg |
Price: | USD80/kg ~ USD120/kg |
Standard Packaging: | Pallets |
Delivery Period: | It depends on the quantity to be ordered. |
Payment Method: | by T/T or L/C, Western Union |
Supply Capacity: | 100,000,000.00 |
The as-cast samples of FSX-414 Co-based superalloy were heat treated at the standard solution and aging heat treatment cycles. Specimens for joining were cut from the as-cast ingot. Transient liquid phase (TLP) bonding was carried out at the standard solution cycle, using MBF-30 interlayer. Also, bonded specimens were homogenized at the standard aging condition
We produce High Temperature Superalloy Castings Parts with centrifugal cast process, precision cast process and resin sand cast process.
Table 1 : Standard Cobalt cobalt alloy Alloy
Co | Cr | C | W | Mo | Ni | Si | B | Fe | Mn | Others | |
cobalt alloy 1 | BAL | 33 | 2.45 | 13 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 3 | BAL | 31 | 2.5 | 13 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 4 | BAL | 31.5 | 1 | 14 | - | 2.0* | 1 | - | 2.0* | 1 | - |
BAL | 28 | 1.2 | 5 | - | 3.0* | 1 | - | 2.5* | 1 | - | |
cobalt alloy 12 | BAL | 29 | 1.85 | 9 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 20 | BAL | 33 | 2.45 | 17.5 | - | 2.5* | 1 | - | 2.5* | 1 | - |
cobalt alloy 21 | BAL | 27 | 0.25 | - | 5.5 | 2.5* | 1 | - | 3.0* | 1 | - |
cobalt alloy 31 | BAL | 26 | 0.5 | 7.5 | - | 10.5 | 1 | - | 2.0* | 1 | - |
cobalt alloy 190 | BAL | 26 | 3.3 | 14 | - | 1.0 | 1 | - | 8.0 | 0.5 | - |
cobalt alloy 238 | BAL | 26 | 0.1 | - | 3 | - | 1 | - | 20.0 | 1 | - |
cobalt alloy 306 | BAL | 25 | 0.4 | 2 | - | 6.0 | 1 | - | 4.0* | 1 | Nb=5 |
94 | BAL | 28 | 1 | 19 | - | 5.0 | 1 | - | 2.5* | 1 | V=1 |
cobalt alloy F | BAL | 25.5 | 1.75 | 12.25 | - | 22.5 | 1 | - | 1.5* | - | - |
cobalt alloy SF1 | BAL | 19 | 1.3 | 13 | - | 13 | 3 | 2.5 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF6 | BAL | 19 | 0.7 | 7 | - | 13 | 2.5 | 1.7 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF12 | BAL | 19 | 1 | 9 | - | 13 | 3 | 2 | 3* | 0.5 | Cu=0.5 |
cobalt alloy SF20 | BAL | 19 | 1.5 | 15 | - | 13 | 3 | 3 | 2* | 0.5 | Cu=0.5 |
TRIBALOY T400 | BAL | 8 | 0.1* | - | 28 | 3* | 2.4 | - | 3* | - | - |
TRIBALOY T800 | BAL | 17 | 0.1* | - | 28 | 3* | 3.2 | - | 3* | - | - |
DELORO 15 | - | - | 0.06* | - | - | BAL | 2.0 | 1.05 | 1.5* | 20 | Cu=20 |
DELORO 22 | - | 0.70 | 0.10 | - | - | BAL | 2.3 | 1.75 | - | - | - |
DELORO 40 | - | 7.0 | 0.10 | - | - | BAL | 3.5 | 2.25 | - | - | - |
DELORO 50 | - | 10.25 | 0.45 | - | - | BAL | 4.0 | 1.85 | 4.0 | - | - |
DELORO 60 | - | 14.25 | 0.6 | - | - | BAL | 2.0 | 3.5 | 4.0 | - | - |
DELORO 625 | - | 22 | 0.1 | - | 9 | BAL | - | - | 5 | - | - |
NISTELLE C | - | 16.5 | 0.12* | 4.5 | 17 | BAL | 0.7 | - | 6.0 | - | - |
TRIBALOY T700 | - | 15 | 0.10* | - | 32 | BAL | 3.25 | - |
Hastelloy C22®(UNS N06022)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V | |
0.015 | 0.5 | 0.02 | 0.02 | 0.08 | 20.0-22.5 | Bal. | 12.5-14.5 | 2.5 | 2.0-6.0 | 2.5-3.5 | 0.35 | |
Hastelloy C276®(UNS N10276)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V | |
0.01 | 1 | 0.04 | 0.03 | 0.08 | 14.5-16.5 | Bal. | 15.0-17.0 | 2.5 | 4.0-7.0 | 3.0-4.5 | 0.35 | |
Hastelloyx®(UNS N06002)(Max.) | ||||||||||||
C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | other | |
0.05-0.15 | 1 | 0.04 | 0.03 | 1 | 20.5-23.0 | Bal. | 8.0-10.0 | 0.5-2.5 | 17.0-20.0 | 0.2-1.0 | / | |
Monel 400®(UNS NO4400) (Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.024 | 0.5 | 63 min | 28-34 | 2.5 | ||||||
Monel M400®(UNS NO4400)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.024 | 0.5 | 63-70 | 28-34 | 2.5 | ||||||
Monel R405®(UNS NO4405)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Fe | ||||||
0.3 | 2 | 0.025-0.06 | 0.5 | 63.0min | 28-34 | 2.5 | ||||||
Monel K500®(UNS NO5500)(Max.) | ||||||||||||
C | MN | S | Si | Ni | Cu | Ti | AI | Fe | ||||
0.1 | 2 | 0.01 | 0.5 | 63min | 27-33 | 0.86 | 2.3-3.15 | 2 | ||||
Inconel 600(UNS NO6600)(Max.) | ||||||||||||
C | MN | S | Si | Cr | Ni | Cu | Fe | |||||
0.15 | 1 | 0.015 | 0.5 | 14-17 | 72 min | 0.5 | 6.0-10.0 | |||||
Inconel 601(UNS NO6601)(Max.) | ||||||||||||
C | MN | Si | Cr | Ni | CO | AI | Fe | |||||
0.05 | 0.3 | 0.2 | 22.5 | 61.5min | 5 | 1.4 | 14.1 | |||||
Inconel 718(UNS NO7718)(Max.) | ||||||||||||
Cr | Ni | Mo | CO | Cb+Ta | Ti | AI | Fe | |||||
19 | 52.5min | 3.05 | 5 | 5.13 | 0.9 | 0.5 | 18.5 | |||||
Chemical Analysis of Incoloy 800® uns(N08800) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.1 max | 19.0-23.0 | 30.0-35.0 | 0.15-0.6 | 0.15-0.6 | 39.5min | / | ||||||
Incoloy800H® UNS(N08810) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.05-0.1 | 19.0-23.0 | 30.0-35.0 | 0.15-0.60 | 0.15-0.60 | 39.5min | 5or coarser | ||||||
Incoloy800HT® UNS(N08811) | ||||||||||||
C | Cr | Ni | Ti | AI | Fe | Grain | ||||||
0.06-0.10 | 19.0-23.0 | 30.0-35.0 | 0.25-0.60 | 0.25-0.60 | 39.5min | 5or coarser | ||||||
Dimensions:as per drawings
Special Features: 1.Good surface finish; 2.We use Precision Cast Process to produce the Cobalt Based Superalloy parts. 3.We do high temperature solution treatment to achieve better wear performance. |
Step 1: Getting orders.
Step 2: Process design by technical department
Step 3: Purchase of raw materials and pattern making &checking
Step 4: Inspection of raw materials
Step 5: Melting by middle-frequency induction furnaces
Step 6: Ladle analysis by Spectrometer
Step 7: De-oxidization, slag-removal, tapping
Step 8: Pouring
Step 9: Openning & fettling
Step 10: Surface & dimensional check
Step 11: Heat treatment
Step 12: Inspection of physical property (UT test,MT test, hardness,impact value µstructure)
Step 13: Packing
Step 14: Shipping
1. 16-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.